0733 Nitrile(NBR)

0733 Nitrile(NBR)

0733 Nitrile(NBR) Rubber Sheeting is a premium, high polymer content material for applications requiring best performance against Oils with excellent resistance to swell and superior mechanical characteristics.

This material is often manufactured with a Milliken Insertion to further enhance the tear resistance and burst strength, especially in high pressure applications.


Accelerated Ageing - Change in Elongation at Break (168 Hours @ 70°C)
-30 %
Accelerated Ageing - Change in Elongation at Break (168 Hours @ 70°C)
-30 %
Accelerated Ageing - Change in Tensile Strength (168 Hours @ 70°C)
+10 %
Accelerated Ageing - Change in Tensile Strength (168 Hours @ 70°C)
+10 %
Accelerated Ageing - Change in Hardness (168 Hours @ 70°C)
+2 ° Shore
Accelerated Ageing - Change in Hardness (168 Hours @ 70°C)
+2 ° Shore
Elongation at Break
600 %
Elongation at Break
600 %
Highest Recommended Working Temperature
90 °C
Highest Recommended Working Temperature
90 °C
Lowest Recommended Working Temperature
-20 °C
Lowest Recommended Working Temperature
-20 °C
Oil Swell IRM901
5 %
Oil Swell IRM901
5 %
Shore Hardness(IRHD)
65 ° Shore
Shore Hardness(IRHD)
65 ° Shore
Specific Gravity
1.32 g/cm3
Specific Gravity
1.32 g/cm3
Superficial Resistivity
3·10 EXP 12 Ohm  
Superficial Resistivity
3·10 EXP 12 Ohm  
Tear Resistance
25 N/mm
Tear Resistance
25 N/mm
Tensile Strength
15 MPA
Tensile Strength
15 MPA
Transversal Resistivity
2.5·10 EXP 9 Ohm·cm  
Transversal Resistivity
2.5·10 EXP 9 Ohm·cm  
Made in European Union
REACH Compliant