J102 Aramid Jointing Material to BS7531 Grade X

J102 Aramid Jointing Material to BS7531 Grade X

A superior quality Grade X Jointing with excellent mechanical properties and a wide range of approvals including DIN-DVGW, WRAS, BAM & BS7531 Grade X


BAM Approved Pressure
160 bar
BAM Approved Pressure
160 bar
BAM Aproved Temperature
90 °C
BAM Aproved Temperature
90 °C
BS7531 Grade
Grade X  
BS7531 Grade
Grade X  
Compression
9 %
Compression
9 %
Density
1.75 g/cc
Density
1.75 g/cc
Gas Leakage
1 cc/min
Gas Leakage
1 cc/min
Highest Recommended Working Temperature
400 °C
Highest Recommended Working Temperature
400 °C
Recovery
55 %
Recovery
55 %
Residual Stress(BS7531 300°C)
26 MPA
Residual Stress(BS7531 300°C)
26 MPA
Residual Stress(DIN52913)
32 MPA
Residual Stress(DIN52913)
32 MPA
Steam Operating Temp Range
250 °C
Steam Operating Temp Range
250 °C
Thickness Increase (ASTM Fuel B)
3 %
Thickness Increase (ASTM Fuel B)
3 %
Thickness Increase (ASTM Oil 1)
1 %
Thickness Increase (ASTM Oil 1)
1 %
Thickness Increase (IRM Oil 903)
2.5 %
Thickness Increase (IRM Oil 903)
2.5 %
Acid Resistance
Chemical Resistant
High Working Temperature
Oil Resistance
Ozone Resitance
Potable Water Suitability
Sea Water Resistance
DIN-DVGW
Made in the UK
REACH Compliant
Water Council Approved